Effect of Cast Iron Structure and Properties on Contact Quality with an Aluminum Electrolyzer Carbon Anode
- Авторы: Babkin V.G.1, Kukartsev V.A.1, Cherepanov A.I.1, Arkhipov G.V.2, Savina A.N.2
-
Учреждения:
- Siberian Federal University
- RUSAL Engineering Center, RUSAL Joint Company
- Выпуск: Том 61, № 3-4 (2017)
- Страницы: 318-324
- Раздел: Article
- URL: https://journal-vniispk.ru/0026-0894/article/view/240241
- DOI: https://doi.org/10.1007/s11015-017-0495-8
- ID: 240241
Цитировать
Аннотация
Physicomechanical and casting properties are studied for high-phosphorus irons used in the assembly of aluminum electrolyzer baked anodes in RUSAL enterprises compared with gray cast iron containing a minimum amount of phosphorus and sulfur. It is shown that iron primary crystallization under conditions approaching pouring production parameters and iron cooling in the nipple – cast iron – carbon anode contact assembly proceeds with significant supercooling that causes the formation of a pearlite matrix in the cast iron structure with increased hardness. Iron with a lower carbon equivalent exhibiting high hardness has a better elasticity modulus and strength values. The presence of ternary phosphide eutectic within the iron structure with a high phosphorus content reduces the breaking strength considerably at high anode operating temperatures and this may be a reason for cast iron loss of strength and anode separation at the end of an operating cycle leading the electrolyzer stoppage. Iron with the minimum phosphorus content exhibits strength exceeding by more than a factor of two that of high-phosphorus cast iron and also the least electrical resistance in the range up to 500–600°C. In addition, iron with a high phosphorus content has an anomalous change in linear thermal expansion coeffi cient (LTEC) in the range 600–810°C that may also lead to degradation of “soft” metal (anode at the end of an operating cycle). The results obtained are explained drawing on thermal analysis data and metallographic studies.
Об авторах
V. Babkin
Siberian Federal University
Автор, ответственный за переписку.
Email: lpiomd@bk.ru
Россия, Krasnoyarsk
V. Kukartsev
Siberian Federal University
Email: lpiomd@bk.ru
Россия, Krasnoyarsk
A. Cherepanov
Siberian Federal University
Email: lpiomd@bk.ru
Россия, Krasnoyarsk
G. Arkhipov
RUSAL Engineering Center, RUSAL Joint Company
Email: lpiomd@bk.ru
Россия, Krasnoyarsk
A. Savina
RUSAL Engineering Center, RUSAL Joint Company
Email: lpiomd@bk.ru
Россия, Krasnoyarsk
Дополнительные файлы