Nitriding of Molten Chromium-Manganese Steels


如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

Theoretical and experimental studies are conducted in the field of nitriding high strength nonmagnetic steels. Temperature-time correlation of the degree nitrogen assimilation and nitrogen content in steel 04Cr20Ni6Mn11Mo2NVNb in the case of alloying with nitrogencontaining manganese and chromium ferroalloys in air and during purging with nitrogen are determined by experiment. Gas phase nitriding of this steel is possible at 1450 °C during 30 min reaching a nitrogen content of 0.42%. A twostage process for lowcost nitriding is developed. In the first stage melts are purged with highpurity nitrogen to reach a nitrogen content of 0.25–0.30%. In the second stage powder alloying additions are injected into a stream of nitrogen with a melt temperature as low as possible.

作者简介

L. Smirnov

Institute of Metallurgy, Ural Section, Russian Academy of Sciences

编辑信件的主要联系方式.
Email: sekretar@uim-stavan.ru
俄罗斯联邦, Ekaterinburg

O. Zayakin

Institute of Metallurgy, Ural Section, Russian Academy of Sciences

Email: sekretar@uim-stavan.ru
俄罗斯联邦, Ekaterinburg

V. Zhuchkov

Institute of Metallurgy, Ural Section, Russian Academy of Sciences

Email: sekretar@uim-stavan.ru
俄罗斯联邦, Ekaterinburg

A. Oryshchenko

NITs Kurchatov Institute, TsNII KM Prometei

Email: sekretar@uim-stavan.ru
俄罗斯联邦, St. Petersburg

G. Kalinin

NITs Kurchatov Institute, TsNII KM Prometei

Email: sekretar@uim-stavan.ru
俄罗斯联邦, St. Petersburg

D. Shul’min

OAO Ural Institute of Metals

Email: sekretar@uim-stavan.ru
俄罗斯联邦, Ekaterinburg

补充文件

附件文件
动作
1. JATS XML

版权所有 © Springer Science+Business Media, LLC, part of Springer Nature, 2019