Thermal Stability of Surface Plasmon Resonance Absorption in а-С:Н〈Ag + TiО2〉 Nanocomposite Films
- 作者: Prikhod’ko O.Y.1, Mikhailova S.L.1, Mukhametkarimov E.S.1, Dautkhan K.1, Maksimova S.Y.1, Ismailova G.A.1, Tauasarov K.A.1, Mikhailov L.V.1
-
隶属关系:
- National Nanotechnology Open Laboratory, Al-Farabi Kazakh National University, NNLOT
- 期: 卷 125, 编号 6 (2018)
- 页面: 864-869
- 栏目: Spectroscopy of Condensed States
- URL: https://journal-vniispk.ru/0030-400X/article/view/165874
- DOI: https://doi.org/10.1134/S0030400X18120160
- ID: 165874
如何引用文章
详细
The thermal stability of surface plasmon resonance in a-C:H〈Ag〉 and a-C:H〈Ag + TiО2〉 nanocomposite films is studied. The films were deposited by ion-plasma magnetron sputtering of a combined graphite-metal target in the atmosphere of the argon and methane mixture. The structure and optical properties of nanocomposite films were studied using transmission electron microscopy and optical spectroscopy, respectively. It is found that surface plasmon resonance in the a-C:H〈Ag + TiО2〉 films persists to the annealing temperature of 450°C in argon atmosphere, whereas in a-C:H〈Ag〉 films, surface plasmon resonance disappears at the annealing temperature of 350°C. It is shown that annealing at 350°C leads to the significant increase in the diameter of silver nanoparticles in the structure of the a-C:H〈Ag〉 films. In the a-C:H〈Ag + TiO2〉 films, along with the appearance of silver nanoparticles with a large diameter, silver nanoparticles with a small diameter are present, which remain after annealing at this temperature. The higher thermal stability of surface plasmon resonance in the a-C:H〈Ag + TiО2〉 films is explained by the presence of TiO2 nanoparticles in the structure of films, which inhibit the coalescence of silver nanoparticles at high temperatures.
作者简介
O. Prikhod’ko
National Nanotechnology Open Laboratory, Al-Farabi Kazakh National University,NNLOT
Email: Svetlana.Mikhailova@kaznu.kz
哈萨克斯坦, Almaty, 050040
S. Mikhailova
National Nanotechnology Open Laboratory, Al-Farabi Kazakh National University,NNLOT
编辑信件的主要联系方式.
Email: Svetlana.Mikhailova@kaznu.kz
哈萨克斯坦, Almaty, 050040
E. Mukhametkarimov
National Nanotechnology Open Laboratory, Al-Farabi Kazakh National University,NNLOT
Email: Svetlana.Mikhailova@kaznu.kz
哈萨克斯坦, Almaty, 050040
K. Dautkhan
National Nanotechnology Open Laboratory, Al-Farabi Kazakh National University,NNLOT
Email: Svetlana.Mikhailova@kaznu.kz
哈萨克斯坦, Almaty, 050040
S. Maksimova
National Nanotechnology Open Laboratory, Al-Farabi Kazakh National University,NNLOT
Email: Svetlana.Mikhailova@kaznu.kz
哈萨克斯坦, Almaty, 050040
G. Ismailova
National Nanotechnology Open Laboratory, Al-Farabi Kazakh National University,NNLOT
Email: Svetlana.Mikhailova@kaznu.kz
哈萨克斯坦, Almaty, 050040
K. Tauasarov
National Nanotechnology Open Laboratory, Al-Farabi Kazakh National University,NNLOT
Email: Svetlana.Mikhailova@kaznu.kz
哈萨克斯坦, Almaty, 050040
L. Mikhailov
National Nanotechnology Open Laboratory, Al-Farabi Kazakh National University,NNLOT
Email: Svetlana.Mikhailova@kaznu.kz
哈萨克斯坦, Almaty, 050040
补充文件