Reactor neutrons irradiation effect on the photocatalytic activity of SnO2 thin films

Abstract

SnO₂ thin films synthesized by sol-gel are irradiated with reactor neutrons up to fast neutron fluence of 9.6 × 10¹⁷ neutrons cm^–2 at 40°C. The influence of defects generated by neutrons irradiation, through the properties modification, on the photo-catalytic activity of SnO₂ films is investigated. It is found that the photoactivity of the irradiated films is enhanced after reactor neutrons irradiation. An improvement of 41% is observed for the sample irradiated at a neutron fluence of 9.6 × 10¹⁷ neutrons cm^–2. This is attributed to several parameters modified by the reactor neutron irradiation principally the crystallite size and space charge region which are closely related to the photocatalytic performance.