XPS Study of the Process of HgCdTe Oxidation in a Glow Discharge Oxygen Plasma
- Авторлар: Zakirov E.R.1, Kesler V.G.1
- 
							Мекемелер: 
							- Rzhanov Institute of Semiconductor Physics, Siberian Branch
 
- Шығарылым: Том 60, № 7 (2019)
- Беттер: 1043-1051
- Бөлім: Article
- URL: https://journal-vniispk.ru/0022-4766/article/view/162143
- DOI: https://doi.org/10.1134/S0022476619070047
- ID: 162143
Дәйексөз келтіру
Аннотация
Initial stages of HgCdTe oxidation in a glow discharge plasma in O2 atmosphere are first studied using the XPS method. The chemical composition of the growing native oxide layer is investigated and the oxidation kinetics is revealed. It is experimentally established that the mechanism of HgCdTe oxidation changes as the oxide thickness reaches 2-3 nm due to the change of the limiting stage of the chemical reaction. The composition of the formed oxide is varies with depth and is characterized by low mercury content. It is suggested that the diffusion of oxygen to the oxide–semiconductor interface and its predominant interaction with tellurium are the main mechanism of the native MCT oxide growth, so that the oxide region bordering the substrate is ∼10% oxygen depleted. The obtained results are discussed and compared with previously reported data on MCT oxidation in RF plasma and in liquid electrolytes.
Негізгі сөздер
Авторлар туралы
E. Zakirov
Rzhanov Institute of Semiconductor Physics, Siberian Branch
							Хат алмасуға жауапты Автор.
							Email: erzakirov@isp.nsc.ru
				                					                																			                												                	Ресей, 							Novosibirsk						
V. Kesler
Rzhanov Institute of Semiconductor Physics, Siberian Branch
														Email: erzakirov@isp.nsc.ru
				                					                																			                												                	Ресей, 							Novosibirsk						
Қосымша файлдар
 
				
			 
						 
						 
						 
					 
						 
									 
  
  
  
  
  Мақаланы E-mail арқылы жіберу
			Мақаланы E-mail арқылы жіберу  Ашық рұқсат
		                                Ашық рұқсат Рұқсат берілді
						Рұқсат берілді Тек жазылушылар үшін
		                                		                                        Тек жазылушылар үшін
		                                					