FILLING OF CHANNELS OF THE ZEOLITE FRAMEWORK IN TRIGONAL POLAR NONABORATE Ва3Na0.9(OH)1.9[B9O16][B(OH)3]

Capa

Citar

Texto integral

Resumo

Crystals of the new trigonal borate Ва3Na0.9(OH)1.9[B9O16][B(OH)3] (sp. gr. P31c, a =10.23684(15) Å, c = 8.72926(13) Å) were prepared by the mild hydrothermal synthesis. The filling of the channels in the framework of the polar nonaborate was found to differ from that determined previously. It is consistent with the main features of this structure type with the preservation of sassoline molecules in the channels. The structure contains an additional ОН group, which is involved in the coordination of Ва.

Sobre autores

A. Topnikova

Lomonosov Moscow State University, Moscow, 119991 Russia

Email: nastya_zorina@rambler.ru
Россия, Москва

E. Belokoneva

Lomonosov Moscow State University, Moscow, 119991 Russia

Email: nastya_zorina@rambler.ru
Россия, Москва

O. Dimitrova

Lomonosov Moscow State University, Moscow, 119991 Russia

Email: nastya_zorina@rambler.ru
Россия, Москва

A. Volkov

Lomonosov Moscow State University, Moscow, 119991 Russia

Email: nastya_zorina@rambler.ru
Россия, Москва

L. Zorina

Osipyan Institute of Solid State Physics, Russian Academy of Sciences, Chernogolovka, Moscow region, 142432 Russia

Autor responsável pela correspondência
Email: nastya_zorina@rambler.ru
Россия, Черноголовка

Bibliografia

  1. The Cambridge Crystallographic Data Centre (CCDC). Inorganic Crystal Structure Data Base – ICSD. https://www.ccdc.cam.ac.uk/, http://www.fiz-karlsruhe.de
  2. Crystallography Open Database. crystallography.net/cod
  3. Christ C.L., Clark J.R. // Phys. Chem. Miner. 1977. V. 2. P. 59.
  4. Liu L., Su X., Yang Y. et al. // Dalton Trans. 2014. V. 43. P. 8905.
  5. Smith R.W., Keszler D.A. // Mater. Res. Bull. 1989. V. 24. P. 725.
  6. Bubnova R.S., Krivovichev S.V., Filatov S.K. et al. // J. Solid State Chem. 2007. V. 180. P. 596.
  7. Белоконева Е.Л., Стефанович С.Ю., Димитрова О.В. // Кристаллография. 2012. Т. 57. С. 70.
  8. Wei Q., Sun L., Zhang J., Yang G.-Y. // Dalton Trans. 2017. V. 46. P. 7911.
  9. Heyward C., McMillen C.D., Kolis J. // J. Solid State Chem. 2013. V. 203. P. 166.
  10. Chen X., Wu L., Chang X., Xiao W. // Solid State Sci. 2014. V. 27. P. 47.
  11. Топникова А.П., Белоконева Е.Л. // Успехи химии. 2019. Т. 88. № 2. С. 204.
  12. Белоконева Е.Л., Стефанович С.Ю., Димитрова О.В. и др. // Кристаллография. 2009. Т. 54. № 5. С. 860.
  13. Agilent (2014). CrysAlis PRO. Agilent Technologies Ltd, Yarnton, Oxfordshire, England.
  14. Sheldrick G.M. // Acta Cryst. A. 2008. V. 64. P. 112.
  15. Farrugia L.J. // J. Appl. Cryst. 2012. V. 45. P. 849.
  16. Белоконева Е.Л., Стефанович С.Ю., Борисова Т.А., Димитрова О.В. // Журн. неорган. химии. 2001. Т. 46. С. 1788.
  17. Sheldrick G.M. // Acta Cryst. C. 2015. V. 71. P. 3.
  18. Dowty E. ATOMS. Shape Software, Kingsport, Tennessee, USA, 2006.
  19. Grube H.H. // Fortsch. Mineral. 1981. B. 59. S. 58.
  20. Lu J., Shi G., Wu H. et al. // RSC Adv. 2017. V. 7. P. 20259.
  21. Wu Ch., Song J., Li L. et al. // J. Mater. Chem. C. 2016. V. 4. P. 8189.
  22. Wei Q., Wang J.-J., He Ch. et al. // Chem. Eur. J. Commun. 2016. V. 22. P. 10759.
  23. Wu Ch., Jiang X., Lin L. et al. // Angew. Chem. Int. Ed. 2021. V. 60. № 52. P. 27151.

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML
Baixar
2.

Baixar (1MB)
Metadados
3.

Baixar (235KB)
Metadados

Declaração de direitos autorais © Russian Academy of Sciences, 2023

Согласие на обработку персональных данных

 

Используя сайт https://journals.rcsi.science, я (далее – «Пользователь» или «Субъект персональных данных») даю согласие на обработку персональных данных на этом сайте (текст Согласия) и на обработку персональных данных с помощью сервиса «Яндекс.Метрика» (текст Согласия).