Influence of Quenching and Partitioning Temperature on Mechanical Properties of Steel 37MnSi5


Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

The influence of the temperature of heating for quenching and subsequent heating for redistribution of carbon between martensite and retained austenite (partitioning) on the mechanical properties of steel 37MnSi5 (35GS) is studied. The tested quenching temperatures are 210, 238 and 270°C and the partitioning temperatures are 300, 400 and 450°C. An optimum combination of strength and ductility exceeding the level of the properties of the steel after standard quenching and tempering or austempering is obtained.

Sobre autores

H. Ghazvinloo

Department of Materials Engineering, Semnan University

Autor responsável pela correspondência
Email: Hamid.Ghazvinloo@gmail.com
Irã, Semnan

A. Honarbakhsh-Raouf

Department of Materials Engineering, Semnan University

Email: Hamid.Ghazvinloo@gmail.com
Irã, Semnan

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML

Declaração de direitos autorais © Springer Science+Business Media, LLC, part of Springer Nature, 2019