Effect of Artificial Aging on the Microstructure and Mechanical Properties of Aluminum Alloy AA6061-T6


Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Somente assinantes

Resumo

The properties of aluminum alloy AA6061-T6 after aging at 220°C for 0.5 – 8 h are studied by the methods of light and scanning electron microscopy and fractography. The mechanical characteristics of the alloy are determined by tensile tests.

Sobre autores

Meysam Toozandehjani

Department of Mechanical Engineering, Faculty of Engineering, Universiti Putra Malaysia

Email: faizalms@upm.edu.my
Malásia, Serdang, Selangor, Darul Ehsan, 43400

Faizal Mustapha

Department of Aerospace Engineering, Faculty of Engineering, Universiti Putra Malaysia

Autor responsável pela correspondência
Email: faizalms@upm.edu.my
Malásia, Serdang, Selangor, Darul Ehsan, 43400

Mohd Ariffin

Department of Mechanical Engineering, Faculty of Engineering, Universiti Putra Malaysia

Email: faizalms@upm.edu.my
Malásia, Serdang, Selangor, Darul Ehsan, 43400

Nur Zahari

Department of Mechanical Engineering, Faculty of Engineering, Universiti Putra Malaysia

Email: faizalms@upm.edu.my
Malásia, Serdang, Selangor, Darul Ehsan, 43400

Khamirul Matori

Materials Synthesis and Characterization Laboratory, Institute of Advanced Technology, Universiti Putra Malaysia; Department of Physics, Faculty of Science, Universiti Putra Malaysia

Email: faizalms@upm.edu.my
Malásia, UPM, Serdang, Selangor, Darul Ehsan, 43400; UPM, Serdang, Selangor, Darul Ehsan, 43400

Farhad Ostovan

Materials Synthesis and Characterization Laboratory, Institute of Advanced Technology, Universiti Putra Malaysia

Email: faizalms@upm.edu.my
Malásia, UPM, Serdang, Selangor, Darul Ehsan, 43400

Firouz Fadaeifard

Materials Synthesis and Characterization Laboratory, Institute of Advanced Technology, Universiti Putra Malaysia

Email: faizalms@upm.edu.my
Malásia, UPM, Serdang, Selangor, Darul Ehsan, 43400

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML

Declaração de direitos autorais © Springer Science+Business Media New York, 2016