Synthesis of IR phosphors based on germanatoborate Gd14Ge2B6O34

Abstract

Processes of the formation of germanatoborates Gd₁₄B₆Ge₂O₃₄ and Gd_13.02Nd_0.98B₆Ge₂O₃₄ have been studied using different methods of synthesis (solid-state interaction, direct and inverse co-precipitation, self-propagating high-temperature synthesis (SHS)). It has been established that the synthesis of germanatoborates Gd₁₄B₆Ge₂O₃₄ and Gd_13.02Nd_0.98B₆Ge₂O₃₄ using the inverse precipitation and SHS methods occurs with the formation of an intermediate apatite-like phase, which upon heating to above 1100°С is reconstructed into the Ln₁₄B₆Ge₂O₃₄ (Ln = Gd, Nd) structure. The germanatoborates synthesized crystallize in the trigonal system (space group P3₁). The lattice parameters of Gd_13.02Nd_0.98B₆Ge₂O₃₄ are a = 9.746(4) Å and c = 25.795(13) Å. The thermal stability of the Gd₁₄B₆Ge₂O₃₄ and Gd_13.02Nd_0.98B₆Ge₂O₃₄ germanatoborates has been studied. The obtained materials of composition Gd_13.02Nd_0.98B₆Ge₂O₃₄ show luminescence properties and can be employed as infrared phosphors.