Glass Formation in the Ternary System La2O3–As2S3–Er2O3
- Авторлар: Bakhtiyarly I.B.1, Fatullaeva G.M.1, Kerimli O.S.1
-
Мекемелер:
- Nagiev Institute of Catalysis and Inorganic Chemistry
- Шығарылым: Том 63, № 7 (2018)
- Беттер: 962-965
- Бөлім: Physicochemical Analysis of Inorganic Systems
- URL: https://journal-vniispk.ru/0036-0236/article/view/168859
- DOI: https://doi.org/10.1134/S0036023618070021
- ID: 168859
Дәйексөз келтіру
Аннотация
The boundaries of the glass formation region in the ternary system La2O3–As2S3–Er2O3 were found. Transparent glass of composition (La2O3)0.03(As2S3)0.90(Er2O3)0.07 was studied by X-ray photoelectron and Raman spectroscopy. The intensities of the bands characterizing As–S, La–O, and Er–O bonds increased, and these bands were shifted toward higher energies. This was due to an increase in the covalence of these bonds and probably due to the formation of new bonds in the glasses. Samples in the glass formation region are resistant at 300 K to air, water, and organic solvents.
Авторлар туралы
I. Bakhtiyarly
Nagiev Institute of Catalysis and Inorganic Chemistry
Хат алмасуға жауапты Автор.
Email: ibbakhtiyarli@mail.ru
Әзірбайжан, Baku, AZ1143
G. Fatullaeva
Nagiev Institute of Catalysis and Inorganic Chemistry
Email: ibbakhtiyarli@mail.ru
Әзірбайжан, Baku, AZ1143
O. Kerimli
Nagiev Institute of Catalysis and Inorganic Chemistry
Email: ibbakhtiyarli@mail.ru
Әзірбайжан, Baku, AZ1143
Қосымша файлдар