Structure and properties of a layered steel/vanadium alloy/steel composite prepared by high-pressure torsion


Дәйексөз келтіру

Толық мәтін

Ашық рұқсат Ашық рұқсат
Рұқсат жабық Рұқсат берілді
Рұқсат жабық Тек жазылушылар үшін

Аннотация

The microstructure and hardness of a layered steel 08Kh17T/V–10Ti–5Cr/steel 08Kh17T composite, which was prepared by torsion under a high hydrostatic pressure at temperatures of 20, 200, and 400°C, have been studied. Severe plastic deformation under used conditions is shown to provide good joining of layers, which is accompanied by their substantial hardening (from 2.0 to 3.5 times). During deformation at temperatures of 20 and 200°C, fragmentation of the vanadium alloy layer into thinner layers is observed; at 400°C, mainly a plane interface between the vanadium alloy and the steel layers is formed.

Авторлар туралы

S. Nikulin

National University of Science and Technology MISiS

Хат алмасуға жауапты Автор.
Email: csaap@mail.ru
Ресей, Leninskii pr. 4, Moscow, 119049

S. Rogachev

National University of Science and Technology MISiS

Email: csaap@mail.ru
Ресей, Leninskii pr. 4, Moscow, 119049

A. Rozhnov

National University of Science and Technology MISiS

Email: csaap@mail.ru
Ресей, Leninskii pr. 4, Moscow, 119049

V. Khatkevich

National University of Science and Technology MISiS

Email: csaap@mail.ru
Ресей, Leninskii pr. 4, Moscow, 119049

T. Nechaikina

National University of Science and Technology MISiS

Email: csaap@mail.ru
Ресей, Leninskii pr. 4, Moscow, 119049

M. Morozov

National University of Science and Technology MISiS

Email: csaap@mail.ru
Ресей, Leninskii pr. 4, Moscow, 119049

Қосымша файлдар

Қосымша файлдар
Әрекет
1. JATS XML

© Pleiades Publishing, Ltd., 2016