Destructive effect of solar light on morphology of colloidal silver nanocubes
- Authors: Ashkarran A.A.1, Daemi S.1, Derakhshi M.1
-
Affiliations:
- Department of Physics, Faculty of Basic Sciences
- Issue: Vol 78, No 5 (2016)
- Pages: 577-585
- Section: Article
- URL: https://journal-vniispk.ru/1061-933X/article/view/200799
- DOI: https://doi.org/10.1134/S1061933X16050021
- ID: 200799
Cite item
Abstract
Colloidal silver nanocubes (NCs) were successfully synthesized by reduction of silver nitrate with ethylene glycol and polyvinylpyrrolidon as capping agent. The effect of solar light irradiation on the formation and morphology of silver NCs was investigated. Moreover, altering the amount of sodium sulfide was used to control the morphology and shape of primary silver seeds. Scanning electron microscopy, transmitting electron microscopy, X-ray diffraction and UV-vis spectroscopy were used to characterize silver NCs. The samples prepared under the solar light irradiation do not possess cubic shape while highly monodispersed silver NCs were obtained in dark room conditions. For dark room synthesis, a decrease of the amount of Na2S by only 10 μL resulted in formation of mixture of silver nanospheres and nanowires in addition to NCs instead of the monodispersed silver NCs. However, similar increase of the amount of sodium sulfide results in distortion of cubic geometry of particles. The results suggest that solar light has a negative effect on the shape evolution of the primary silver seeds.
About the authors
Ali Akbar Ashkarran
Department of Physics, Faculty of Basic Sciences
Author for correspondence.
Email: ashkarran@umz.ac.ir
Iran, Islamic Republic of, Babolsar
Sahar Daemi
Department of Physics, Faculty of Basic Sciences
Email: ashkarran@umz.ac.ir
Iran, Islamic Republic of, Babolsar
Maryam Derakhshi
Department of Physics, Faculty of Basic Sciences
Email: ashkarran@umz.ac.ir
Iran, Islamic Republic of, Babolsar
Supplementary files