Ionic conductivity of ScF3 single crystals (ReO3 type)

Abstract

Electrical conductivity σ of ScF₃ single crystals (sp. gr. \(Pm\overline 3 m\), ReO₃ structure type) has been studied by impedance spectroscopy and compared with the electrical conductivity of rare earth HoF₃ (β-YF₃ type) and LaF₃ (tysonite type) trifluorides. ScF₃ crystals obtained by Bridgman directional solidification have ionic conductivity σ = 4 × 10^–8 S/cm at 673 K. It is smaller than the σ values for LaF₃ (sp. gr. \(P\overline 3 c1\)) and HoF₃ (sp. gr. Pnma) single crystals by a factor of 10⁴–10⁵. The low conductivity of ScF₃ crystals is due to the weak coordinating ability (coordination number CN = 6) and low electronic polarizability (α_cat = 1.1 ų) of Sc³⁺ ions. Mobile V_F⁺ vacancies and less mobile interstitial V_i^- ions (defects are formed according to the Frenkel mechanism) are involved in the ion transport. HoF₃ and LaF₃ single crystals have a high coordinating ability (CN = 9 for Ho³⁺ and CN = 11 for La³⁺) and a high electronic polarizability of cations (α_cat = 1.6–1.9 ų for Ho³⁺ and α_cat = 2.2 ų for La³⁺). Only mobile V_F⁺ vacancies (defects are formed according to the Schottky mechanism) are involved in ion transport.