Deposition of stoichiometric Bi2Se3 film by vacuum-thermal treatment of Se/Bi heterostructure

Аннотация

The possibility of obtaining a stoichiometric Bi₂Se₃ film by vacuum-thermal treatment of a Se/Bi heterostructure is demonstrated for the first time. It was found that a stoichiometric Bi₂Se₃ film can be only produced at a certain ratio of the Se and Bi film thicknesses (d_Se/d_Bi = 3.13). X-ray-diffraction analysis and Raman spectroscopy were used to study the phase transformations in a Se(141 nm)/Bi(45 nm) heterostructure upon its thermal treatment in a vacuum. The phase transition temperatures at which various crystalline phases are formed were determined. It is shown that Bi₂Se₃ crystallizes in the Se(141 nm)/Bi(45 nm) heterostructure heated to 493 K in conformity with an exponential law, with a characteristic time in which the equilibrium state is attained equal to 20 min.