A study of planar structures formed on the modified Al2O3 surfaces determining the topology of superconducting elements during YBa2Cu3O7–d deposition

Resumo

We investigate the structural and electrical properties of planar superconducting structures based on the YBa₂Cu₃O_7–d (YBCO) epitaxial films obtained by preliminary modification of the substrate surface. A special master mask was formed on the substrates, so that, at the standard YBCO film deposition onto such a substrate, an insulator layer grew in the modified areas and a superconducting film, in the unmodified ones. Thus, the planar superconducting structure of a desired topology was formed, and the YBCO deposition finished the process. Using this technique, YBCO bridges with widths of 4, 10, and 50 μm on films of different thicknesses and a planar inductive coil were formed. The superconducting transition temperature of the bridges was about 90 K, and the critical current density at a temperature of 77 K was up to 3 MA/cm². The Q factor of the planar inductive coil at a frequency of 85 MHz was 53000 at a temperature of 77 K.