Wear Resistance of Amorphous-Crystalline Coatings with Lubricants

Abstract

The results of tests of a Zr–Al–B boundary friction detonation coating in a wide range of changes under friction conditions have been presented. A comparative analysis of the obtained characteristics of friction and wear in order to evaluate the tribotechnical properties of amorphous-crystalline coatings has been carried out. These results have been compared with parallel tests of coatings based on tungsten carbide, samples of hardened steel and bronze, and the bearing of the sliding layer. The formation of solid solutions has been established and the introduction of oxygen in zirconium that corresponds to the formation on the friction surfaces of the secondary structures of the first type, a characteristic feature of which is their surface localization, ultra-dispersed structure, and ability to minimize disruption and shield unacceptable adhesion phenomena. The use of the Auger electron microscope confirmed that oxygen completely replaces the sulfur in the surface structures.