Investigation of the Fracture and Strength of a Compound with a Carbide Base of a Wear-Resistant Ion-Plasma Vacuum-Arc Ti–N, Ti–Al–N, Ti–Al–Cr–N, and Ti–Al–Ni–N Coatings by the Scratch Testing

I. V. Blinkov; D. S. Belov; A. O. Volkhonskii; A. V. Chernogor; V. S. Sergevnin; A. P. Demirov

doi:10.3103/S1068366619020028

Investigation of the Fracture and Strength of a Compound with a Carbide Base of a Wear-Resistant Ion-Plasma Vacuum-Arc Ti–N, Ti–Al–N, Ti–Al–Cr–N, and Ti–Al–Ni–N Coatings by the Scratch Testing

Authors: Blinkov I.V.¹, Belov D.S.¹, Volkhonskii A.O.¹, Chernogor A.V.¹, Sergevnin V.S.¹, Demirov A.P.¹
Affiliations:
1. National University of Science and Technology MISiS
Issue: Vol 40, No 2 (2019)
Pages: 171-178
Section: Article
URL: https://journal-vniispk.ru/1068-3666/article/view/229281
DOI: https://doi.org/10.3103/S1068366619020028
ID: 229281

Cite item

Full Text

Open Access
Restricted Access

Access granted
Restricted Access

Subscription Access

Abstract
About the authors
References
Supplementary files
Statistics

Abstract

Comparative studies of the fracture behavior and adhesion strength during scratch testing of a wear-resistant ion-plasma vacuum-arc Ti–N, Ti–Al–N, Ti–Al–Cr–N, and Ti–Al–Ni–N coatings are carried out by the scratch test. The type of failure and the adhesion strength characteristics of the coatings based on L_C1, L_C2, and L_C3 are determined by their structure, by the H³/E ² and H/E parameter values, and by the values of compressive macrostresses.