Formation and tribological properties of composite Langmuir–Blodgett films of stearic acid with molybdenum disulfide and amorphous carbon

Abstract

The morphology and tribological properties of Langmuir–Blodgett mono- and bilayers of stearic acid with particles of molybdenum disulfide (MoS₂) and amorphous carbon (С), prepared on silicon and steel substrates by horizontal deposition (stearic acid–MoS₂ and stearic acid–С monolayers) and by the “roll” technique (stearic acid–MoS₂/stearic acid–С bilayers), were studied. Incorporation of C and MoS₂ particles into the structure of a stearic acid film enhances its wear resistance by a factor of 2.8 and 5.5, respectively. The presence of MoS₂ and С particles and of their aggregates of size from ~220 nm to 16.3 μm in stearic acid layers was confirmed by atomic force microscopy.