Stages in Multilayer Carbon Nanotube Formation with Mechanical Activation of Amorphous Carbon
- Autores: Reva V.P.1, Filatenkov A.É.1, Mansurov Y.N.1, Kuryavyi V.G.2
-
Afiliações:
- FGAOU VPO Far-East Federal University
- FGBUN Institute of Chemistry, Far-Eastern Division of the Russian Academy of Sciences
- Edição: Volume 57, Nº 2 (2016)
- Páginas: 141-145
- Seção: Article
- URL: https://journal-vniispk.ru/1083-4877/article/view/248251
- DOI: https://doi.org/10.1007/s11148-016-9943-4
- ID: 248251
Citar
Resumo
Stages of multilayer carbon nanotube formation are studied during mechanical activation of amorphous carbon prepared by pyrolysis from plant raw material. It is shown that prolonged mechanical activation of a carbon composite in a vario-planetary mill (>36 h) leads to formation of aggregates and loss of nanotube thermal stability.
Palavras-chave
Sobre autores
V. Reva
FGAOU VPO Far-East Federal University
Autor responsável pela correspondência
Email: festurvp@mail.ru
Rússia, Vladivostok
A. Filatenkov
FGAOU VPO Far-East Federal University
Email: festurvp@mail.ru
Rússia, Vladivostok
Yu. Mansurov
FGAOU VPO Far-East Federal University
Email: festurvp@mail.ru
Rússia, Vladivostok
V. Kuryavyi
FGBUN Institute of Chemistry, Far-Eastern Division of the Russian Academy of Sciences
Email: festurvp@mail.ru
Rússia, Vladivostok
Arquivos suplementares