Effect of Milling and Sintering Temperature of TaC–TaB2 Composite on Lattice Parameter and C/Ta Ratio
- 作者: Mehdikhan B.1, Borhani G.H.1, Bakhshi S.R.1, Baharvandi H.R.1
-
隶属关系:
- Department of Materials Engineering, Malek-e-ashtar University of Technology
- 期: 卷 57, 编号 5 (2017)
- 页面: 507-512
- 栏目: Article
- URL: https://journal-vniispk.ru/1083-4877/article/view/248561
- DOI: https://doi.org/10.1007/s11148-017-0013-3
- ID: 248561
如何引用文章
详细
The lattice parameter of TaC–TaB2 balk prepared by mechano-chemical and spark plasma sintering (SPS) was investigated by the Nelson–Riley method. In this study, TaC–B4C powder was milled for 3, 6, 9, 12 hours and sintered by spark plasma sintering. The lattice parameter and C/Ta ratio of TaC–TaB2 was calculated by the Nelson–Riley method and the Storms relation. In this research, TaC–B4C powder was reacted and produced TaC–TaB2 composite. Phase formation and powder morphology during milling and sintering were examined using different analysis techniques including XRD and FE-SEM. The lattice parameter of the powders was increased by milling time and sintering temperature.
作者简介
B. Mehdikhan
Department of Materials Engineering, Malek-e-ashtar University of Technology
编辑信件的主要联系方式.
Email: beh_mehdikhani@yahoo.com
伊朗伊斯兰共和国, Isfahan
G. Borhani
Department of Materials Engineering, Malek-e-ashtar University of Technology
Email: beh_mehdikhani@yahoo.com
伊朗伊斯兰共和国, Isfahan
S. Bakhshi
Department of Materials Engineering, Malek-e-ashtar University of Technology
Email: beh_mehdikhani@yahoo.com
伊朗伊斯兰共和国, Isfahan
H. Baharvandi
Department of Materials Engineering, Malek-e-ashtar University of Technology
Email: beh_mehdikhani@yahoo.com
伊朗伊斯兰共和国, Tehran
补充文件