Phase Formation in the Synthesis of Ti2AlN by Spark Plasma Sintering in the Ti/AlN System
- Authors: Gilev V.G.1, Kachenyuk M.N.1
-
Affiliations:
- Perm National Research Polytechnic University
- Issue: Vol 59, No 6 (2019)
- Pages: 658-662
- Section: Article
- URL: https://journal-vniispk.ru/1083-4877/article/view/249195
- DOI: https://doi.org/10.1007/s11148-019-00291-4
- ID: 249195
Cite item
Abstract
The synthesis of a Ti2AlN-based material by mechanical activation (MA) of a Ti–AlN powder mixture in a planetary ball mill followed by vacuum spark plasma sintering (SPS) is investigated. It was shown that the AlN/Ti ratio gradually decreases under mechanical activation. Data on the sample’s phase composition, density and hardness after SPS are given. The maximum content of Ti2AlN at 90 wt.% is achieved at SPS temperature of 1300°C. The lowest porosity of samples at 1.9% is achieved at SPS temperature of 1200 – 1300°C, and the hardness HV0.5 in this case is close to 7 GPa.
About the authors
V. G. Gilev
Perm National Research Polytechnic University
Author for correspondence.
Email: Xray@pm.pstu.ac.ru
Russian Federation, Perm
M. N. Kachenyuk
Perm National Research Polytechnic University
Email: Xray@pm.pstu.ac.ru
Russian Federation, Perm
Supplementary files