Evaluation of the Crack Resistance of Reactive Sintered Composite Boron Carbide-Based Materials
- Авторлар: Perevislov S.N.1
-
Мекемелер:
- I. V. Grebenshchikov Institute of Silicate Chemistry of the Russian Academy of Sciences
- Шығарылым: Том 60, № 2 (2019)
- Беттер: 168-173
- Бөлім: Article
- URL: https://journal-vniispk.ru/1083-4877/article/view/249266
- DOI: https://doi.org/10.1007/s11148-019-00330-0
- ID: 249266
Дәйексөз келтіру
Аннотация
The results of studying the crack resistance of reaction-sintered B4C–SiC composite materials impregnated with liquid silicon with identification and fracture methods are presented. With an increase in the amount of B4C in the reaction-sintered material, its fragility increases. The crack resistance of the material can be increased from 3.40 to 4.02 MPa·m1/2 (when tested by different methods) by adding to the composite material up to 30 wt.% SiC. The material is destroyed mainly by the intercrystalline (intergranular) mechanism. Ceramics containing more than 90 wt.% B4C, is partially destroyed by the transcrystalline mechanism.
Авторлар туралы
S. Perevislov
I. V. Grebenshchikov Institute of Silicate Chemistry of the Russian Academy of Sciences
Хат алмасуға жауапты Автор.
Email: perevislov@mail.ru
Ресей, St. Petersburg
Қосымша файлдар