X-ray Diffraction Tests of Near-Surface Layer of Copper Treated by Ball Rolling

Abstract

The characteristic parameters of the grain-boundary structure and the internal strain values are determined via X-ray diffraction in copper samples exposed to ball rolling. The characteristic coherence length is found to be 75–100 nm and the root-mean-square internal strains are ~1 × 10^–3. The found values are close to those obtained after other types of severe plastic deformation, such as equal-channel angular pressing.