Enviar artigo por via de e-mail Effect of Aging on the Microstructure and Mechanical Properties of Magnesium Alloy AZ31
- Autores: Kerenciler H.1, Gündüz S.2, Erden M.A.2, Türkmen M.3, Karabulut H.4
-
Afiliações:
- Karabük University, Institute of Science and Technology, Department of Manufacturing Engineering
- Karabük University, Technology Faculty, Department of Manufacturing Engineering
- Kocaeli Iniversity, Hereke Vocational School, Department of Metallurgy
- Karabük University, Vocational School, Department of Occupational Health and Safety
- Edição: Volume 58, Nº 3-4 (2016)
- Páginas: 179-184
- Seção: Article
- URL: https://journal-vniispk.ru/0026-0673/article/view/235449
- DOI: https://doi.org/10.1007/s11041-016-9985-8
- ID: 235449
Citar
Acesso aberto
Acesso está concedido
Somente assinantes
Resumo
The structure and mechanical properties of magnesium alloy AZ31 are studied after conventional and deformation aging under conditions corresponding to the thermal cycle of polymerization in paint coating of cars. The aging is conducted after 3-h solution treatment at 400°C, water quenching, and aging at 180°C for from 10 min to 6 h. Some of the specimens are deformed by 0.5% right after the solution treatment and then aged by the same regime.
Sobre autores
H. Kerenciler
Karabük University, Institute of Science and Technology, Department of Manufacturing Engineering
Autor responsável pela correspondência
Email: kerencihuseyin@gmail.com
Turquia, Karabük
S. Gündüz
Karabük University, Technology Faculty, Department of Manufacturing Engineering
Email: kerencihuseyin@gmail.com
Turquia, Karabük
M. Erden
Karabük University, Technology Faculty, Department of Manufacturing Engineering
Email: kerencihuseyin@gmail.com
Turquia, Karabük
M. Türkmen
Kocaeli Iniversity, Hereke Vocational School, Department of Metallurgy
Email: kerencihuseyin@gmail.com
Turquia, Kocaeli-Gebze
H. Karabulut
Karabük University, Vocational School, Department of Occupational Health and Safety
Email: kerencihuseyin@gmail.com
Turquia, Karabük
Arquivos suplementares