A New Approach to Heat Treatment of High-Strength Powder Steels
- Autores: Bidulský R.1, Bidulská J.1, Grande M.A.2
-
Afiliações:
- Technical University of Košice, Faculty of Metallurgy, Department of Metals Forming
- Politecnico di Torino, Department of Applied Science and Technology
- Edição: Volume 58, Nº 11-12 (2017)
- Páginas: 734-737
- Seção: Heat Treatment
- URL: https://journal-vniispk.ru/0026-0673/article/view/236103
- DOI: https://doi.org/10.1007/s11041-017-0087-z
- ID: 236103
Citar
Resumo
Wear (pin-on-disk) tests of low-alloy powder steels (with 0.5 and 0.65% C) are performed after vacuum sintering combined with hardening. The studied alloying systems are 0.65% C + 1.5% Cr + 0.2% Mo, 0.65% C + 0.9% Ni + 0.9% Mo + 0.2% Mn and 0.5% C + 4% Ni + 1.5% Cu + 0.5% Mo. The wear resistance of the steels after the hardening sintering is an order of magnitude higher than after the conventional sintering. The wear resistance of the steels increases in the following order: pearlitic, pearlitic-bainitic, and martensitic structures. Accordingly, the hardness grows from 98 to 105 HRB.
Sobre autores
R. Bidulský
Technical University of Košice, Faculty of Metallurgy, Department of Metals Forming
Autor responsável pela correspondência
Email: robert.bidulsky@tuke.sk
Eslováquia, Košice
J. Bidulská
Technical University of Košice, Faculty of Metallurgy, Department of Metals Forming
Email: robert.bidulsky@tuke.sk
Eslováquia, Košice
M. Grande
Politecnico di Torino, Department of Applied Science and Technology
Email: robert.bidulsky@tuke.sk
Itália, Alessandria
Arquivos suplementares