Hydrothermal synthesis and microstructure of α-Zn2SiO4:V crystal phosphor
- Authors: Zaitseva N.A.1, Krasnenko T.I.1, Onufrieva T.A.1, Samigullina R.F.1
-
Affiliations:
- Institute of Solid State Chemistry, Ural Branch
- Issue: Vol 62, No 2 (2017)
- Pages: 168-171
- Section: Synthesis and Properties of Inorganic Compounds
- URL: https://journal-vniispk.ru/0036-0236/article/view/167363
- DOI: https://doi.org/10.1134/S0036023617020218
- ID: 167363
Cite item
Abstract
A morphologically uniform single-phase crystal phosphor α-Zn2SiO4:V was prepared by one-pot hydrothermal synthesis. Energy dispersive analysis showed that a zinc silicate-base solid solution was formed with a vanadium content of 10 ± 1 at %. Its luminescence spectrum was a broad luminescence band in the region 400–700 nm with a peak near 540 nm.
About the authors
N. A. Zaitseva
Institute of Solid State Chemistry, Ural Branch
Author for correspondence.
Email: natalzay@yandex.ru
Russian Federation, ul. Pervomaiskaya 91, Yekaterinburg, 620990
T. I. Krasnenko
Institute of Solid State Chemistry, Ural Branch
Email: natalzay@yandex.ru
Russian Federation, ul. Pervomaiskaya 91, Yekaterinburg, 620990
T. A. Onufrieva
Institute of Solid State Chemistry, Ural Branch
Email: natalzay@yandex.ru
Russian Federation, ul. Pervomaiskaya 91, Yekaterinburg, 620990
R. F. Samigullina
Institute of Solid State Chemistry, Ural Branch
Email: natalzay@yandex.ru
Russian Federation, ul. Pervomaiskaya 91, Yekaterinburg, 620990
Supplementary files