电邮这篇文章 Dynamic viscoelastic properties of polymeric constructional materials based on polycarbonate
- 作者: Nizhegorodov VV1
-
隶属关系:
- MSTU MAMI
- 期: 卷 1, 编号 2 (2007)
- 页面: 192-195
- 栏目: Articles
- URL: https://journal-vniispk.ru/2074-0530/article/view/69707
- DOI: https://doi.org/10.17816/2074-0530-69707
- ID: 69707
如何引用文章
全文:
详细
The paper presents the research of viscoelastic properties of polymeric constructional materials based on polycarbonate using the methods of acoustic spectroscopy. The research was conducted using the method of free torsional vibrations at the low-frequency acoustic spectrometry, performed on the basis of inverse torsion pendulum. In the measurement process the dynamic shear modulus G 'and mechanical loss-angle tangent tgδ have been obtained. Measurements were performed in a wide temperature range from -180 to 200 ° C. It was shown that the reduction of impact strength at low temperature area is connected with the difference in chemical structure and the introduction of impact modifier.
参考
- Перепечко И.И. Свойства полимеров при низких температурах.− М., 1977.−271с.
- Мэнсон Дж, Сперлинг Л., Полимерные смеси и композиты М.: Химия,1979,− 440с.
- Полимерные смеси, под ред. Д. Пола, С. Ньюмена, пер. с англ. Т. 1, 2, М., 1981,− 1008 с.
- Максимов А.В., Кузьмин В.П., Перепечко И.И. Автоматизированная установка для определения динамических характеристик полимерных материалов// Высокомолек. соединения. Сер.А.−1989.−Т.31. №9. С.1912−1913.
- Перепечко И.И., Данилов В.А., Нижегородов В.В., Бессонова Н.П., Конюхова Е.В. Вязкоупругое поведение и релаксационные процессы в смесях поликарбонат- полибутилентерефталат// Высокомолол. соединения. .−1993.−Т.35. №2. С.174−177.
补充文件