Email this article Study of the Effect of Trace Mg Additions on Carbides in Die Steel H13
- Authors: Li J.1, Li J.1, Wang L.1, Zhu Q.1
-
Affiliations:
- State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
- Issue: Vol 58, No 5-6 (2016)
- Pages: 330-334
- Section: Article
- URL: https://journal-vniispk.ru/0026-0673/article/view/234932
- DOI: https://doi.org/10.1007/s11041-016-0012-x
- ID: 234932
Cite item
Open Access
Access granted
Subscription Access
Abstract
Carbides in annealed steel H13 without magnesium and with a micro-addition of magnesium (0.0010%) are studied. Trace amounts of magnesium strengthen carbide segregation and reduce their size. Carbides phases M7C3, M6 C, and M(C, N) are detected in steel H13, and this agrees with results of thermodynamic calculations.
About the authors
Ji Li
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Email: lijing@ustb.edu.cn
China, Beijing
Jing Li
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Author for correspondence.
Email: lijing@ustb.edu.cn
China, Beijing
Liang-liang Wang
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Email: lijing@ustb.edu.cn
China, Beijing
Qin-tian Zhu
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Email: lijing@ustb.edu.cn
China, Beijing
Supplementary files