Отправить статью по E-mail Study of the Effect of Trace Mg Additions on Carbides in Die Steel H13
- Авторы: Li J.1, Li J.1, Wang L.1, Zhu Q.1
-
Учреждения:
- State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
- Выпуск: Том 58, № 5-6 (2016)
- Страницы: 330-334
- Раздел: Article
- URL: https://journal-vniispk.ru/0026-0673/article/view/234932
- DOI: https://doi.org/10.1007/s11041-016-0012-x
- ID: 234932
Цитировать
Открытый доступ
Доступ предоставлен
Только для подписчиков
Аннотация
Carbides in annealed steel H13 without magnesium and with a micro-addition of magnesium (0.0010%) are studied. Trace amounts of magnesium strengthen carbide segregation and reduce their size. Carbides phases M7C3, M6 C, and M(C, N) are detected in steel H13, and this agrees with results of thermodynamic calculations.
Об авторах
Ji Li
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Email: lijing@ustb.edu.cn
Китай, Beijing
Jing Li
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Автор, ответственный за переписку.
Email: lijing@ustb.edu.cn
Китай, Beijing
Liang-liang Wang
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Email: lijing@ustb.edu.cn
Китай, Beijing
Qin-tian Zhu
State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing
Email: lijing@ustb.edu.cn
Китай, Beijing
Дополнительные файлы